Aluminum Anodizing Surface Appearance2016-04-25


When it comes to aluminum surface treatments, we recommend anodizing mainly for cosmetic appearance purpose. There are generally two types of aluminum anodizing. One is conventional anodizing (MIL-A-8625 Type II), the other one is hard coat anodizing (MIL-A-8625 Type III). When a part is anodized, the anodizing does not only build up the 0.005 - 0.0008 mm thick aluminum oxide on the surface. It also penetrates into the raw material to the same depth.

 

 

What is aluminum anodizing?

 

The anodizing layer is proceeded with the direct current through an electrolytic solution, with an aluminum object serving as an anode. Aluminum anodizing is to build up the thickness of oxide layer on its surface to improve the capability of anti-corrosion and wear. After the anodizing process, the aluminum oxide layer is with improved adhesion of paint primers and glues on the bare metal.  

 

The common method, Type II anodizing, applies an aluminum oxide layer that is generally 0.005 - 0.025 mm thick. In comparison to Type II anodizing, Type III anodize, as known as hard coating, can do 0.050 mm (+/-20%) thickness. Besides, the hard anodized items usually have bronze, gray or black finish. The color can vary depending on the purity of the aluminum substrate. Furthermore, hard anodizing will make the aluminum alloy more resistant to corrosion. The thicker an oxidized layer is, the more effectively it can protect the finished part from moisture, oxygen, and other factors.

 

 

The quality of aluminum anodize coating

 

As time goes by, the quality of anodized layer might get worse. Not only anodized parts stored in high salty and humidity environment affects the quality of anodized layer, but poor quality of anodize solutions used in coating process also poses a negative effect. As for good aluminum anodizing, the surface appearance should be glossy and silk like. 

 

Surface Appearance after Black Anodizing

 Black Anodizing on CNC Milling Part 

 

Below photo shows the comparison of poor quality anodizing(left) and good one(right). We can easily tell the difference based on color, surface quality. In general, the defected anodizing one is with dirty grey, slightly brown color, scratched surface.

 

Surface Appearance after Aluminum Anodizing

 Different Surface Appearance after Anodizing 

 

 

Teflon impregnating after anodizing

 

Instead of anodizing, we can also provide Teflon impregnation service. Our Teflon impregnation process produces a continuous layer of Teflon bonded to the anodized part surface. The Teflon layer is to offer significantly great lubricity and corrosion resistance.

 

Taiwan OEM Customized CNC Milling Aluminum 6061 T6 Black Hard Anodized Teflon Impregnate Mount Bracket Slide Lock

 Teflon Impregnated Aluminum Part with black hard anodizing 

 

 

Send us email if you have any questions about surface treatment of the CNC machining aluminum parts. Also feel free to send us RFQ for free project reviewing.